-65%Li-Ion Battery Cathode - Aluminum Foil Single Side Coated by Li-NCM (9:0.5:0.5 ) (241mm L x 200mm W) 5 sheets/bag - bcaf-ncm911ss—
$248.00
$86.80The Story
This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (Ni:Co:Mn = 9 :0.5:0.5, NCM911) on a single side and can be used as the cathode of Li-Ion battery -- 5 sheets /bag
SPECIFICATIONS
- Material: LiNiCoMnO2 （9:0.5:0.5)
- Current collector (substrate): Aluminum foil (16 microns, area density of 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Single sides area density: 10.5 ± 0.20 mg/cm2
- Compaction density: 3.0 ± 0.1 g/cm3
- Coating Thickness: ~35 um
- Total Thickness: ~51 um
- Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 202 mAh/g
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation
for NCM for AluminumDescription
This electrode sheet is based on Aluminum foil coated by Lithium Nickel Manganese Cobalt Oxide (Ni:Co:Mn = 9 :0.5:0.5, NCM911) on a single side and can be used as the cathode of Li-Ion battery -- 5 sheets /bag
SPECIFICATIONS
- Material: LiNiCoMnO2 （9:0.5:0.5)
- Current collector (substrate): Aluminum foil (16 microns, area density of 4.22mg/cm2)
- Coated Area: 241mm L x 175mm W. The edge width of blank area is 12.5 mm for each side.
- Single sides area density: 10.5 ± 0.20 mg/cm2
- Compaction density: 3.0 ± 0.1 g/cm3
- Coating Thickness: ~35 um
- Total Thickness: ~51 um
- Active Material Proportion in Powder: 95% (PVDF and Super P is 2% and 3%, respectively)
- Specific Capacity: 202 mAh/g
Note: The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation