Li-S Battery Cathode - Aluminum Foil Double Side Coated by Sulfur-Carbon (S/C) Composite (80mm L x 50mm W), 5 sheets/bag - bcaf-SCC-ds

This electrode sheet is based on Aluminum foil coated by S/C composite. Sulfur-Carbon Composite (S/C) with high conductivity and uniform mixing features can be used as high performance cathode for Li-S battery testing

SPECIFICATIONS

• Material: S/C Composite 
• Current collector (substrate): Aluminum foil (16 microns, area density of 4.22mg/cm2)
• Coated Area: 80mm L x 50mm W.
  
• Double sides area density: 8.2 ± 0.2 mg/cm2
• Compaction density: 3.4 ± 0.1 g/cm3
• Coating Thickness: ~66 um
• Total Thickness: ~82 um
• S/C Material Weight: 8.23 g
• S/C Material Proportion in Slurry: 94% (S/C mass ratio is 7:3)
• Specific Capacity: ~1260 mAh/g (0.25C), ~1100 mAh/g (0.5C).
• SDS: Please click to view the Safety Data Sheet

• Note:  The electrode sheet shall be stored in a vacuum box, a vacuum oven or a glove box to avoid degradation.