Double-Side Coated Na3V2(PO4)3 for Sodium Ion Battery Cathode (241 L x 200 W x 0.15 T, mm), 5 sheets/bag - bcaf-NVPds
HomeStore

Double-Side Coated Na3V2(PO4)3 for Sodium Ion Battery Cathode (241 L x 200 W x 0.15 T, mm), 5 sheets/bag - bcaf-NVPds

Double-Side Coated Na3V2(PO4)3 for Sodium Ion Battery Cathode (241 L x 200 W x 0.15 T, mm), 5 sheets/bag - bcaf-NVPds

$93.80

Original: $268.00

-65%
Double-Side Coated Na3V2(PO4)3 for Sodium Ion Battery Cathode (241 L x 200 W x 0.15 T, mm), 5 sheets/bag - bcaf-NVPds—

$268.00

$93.80

The Story

This electrode sheet is a double side-coated layered oxide Na3V2(PO4)3 on aluminum foil and is used as cathodes in Na-Ion battery.
There are 5 sheets in a package bag.

SPECIFICATIONS:

  • Total Area: 241 mm L x 200 mm W x 150 um T
  • Coating Area: 241 mm L x 175 mm W (Left and Right-hand side 12.5 mm without coating)
  • Double side coating
  • Current collector (substrate): Aluminum foil, 15-16 um thickness
  • Coating area density: 9.0 mg/cm2
  • Compaction density: 1.5 g/cm3
  • Coating thickness: ~60 um
  • Active Material Proportion: 92.0% (PVDF, Super P, and CNT is 5%, 2%, and 1%, respectively)
  • Specific Capacity: 106 mAh/g

                 

  • Qty: 5 sheets / bag
  • Warning: Please dry in vacuum oven before using and store it inside glovebox after opening the package
  •  SDS for Aluminum Foil
  • Application Note:
    • Please baking at 80-100 °C under a vacuum oven before coating.
    • MTI does not manufacture this product. We only provide a small quantity to research to develop a new generation battery,
    • MTI is not responsible for any IP issues. If anyone feels the product conflict with your IP, please inform us, we may stop selling at any time.

Description

This electrode sheet is a double side-coated layered oxide Na3V2(PO4)3 on aluminum foil and is used as cathodes in Na-Ion battery.
There are 5 sheets in a package bag.

SPECIFICATIONS:

  • Total Area: 241 mm L x 200 mm W x 150 um T
  • Coating Area: 241 mm L x 175 mm W (Left and Right-hand side 12.5 mm without coating)
  • Double side coating
  • Current collector (substrate): Aluminum foil, 15-16 um thickness
  • Coating area density: 9.0 mg/cm2
  • Compaction density: 1.5 g/cm3
  • Coating thickness: ~60 um
  • Active Material Proportion: 92.0% (PVDF, Super P, and CNT is 5%, 2%, and 1%, respectively)
  • Specific Capacity: 106 mAh/g

                 

  • Qty: 5 sheets / bag
  • Warning: Please dry in vacuum oven before using and store it inside glovebox after opening the package
  •  SDS for Aluminum Foil
  • Application Note:
    • Please baking at 80-100 °C under a vacuum oven before coating.