Double Side LiNiCoMnO2 (Ni:Co:Mn=5:2:3, NCM523) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM523
HomeStore

Double Side LiNiCoMnO2 (Ni:Co:Mn=5:2:3, NCM523) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM523

Double Side LiNiCoMnO2 (Ni:Co:Mn=5:2:3, NCM523) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM523

$521.50

Original: $1,490.00

-65%
Double Side LiNiCoMnO2 (Ni:Co:Mn=5:2:3, NCM523) Coated Aluminum Foil for Battery Cathode (20 m L x 200mm W x 100 um T), 1 Roll, CAl-R-NCM523—

$1,490.00

$521.50

The Story

The NCM523-coated aluminum foil in a roll can be used as cathode for pouch cell testing. 

SPECIFICATIONS

NCM523 coating
  • Coating Thickness: ~88 um (double side coated) 
  • Total Thickness: ~103 um
    Foil Thickness: ~15-16 um
  • Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
  • Double sides material density: 23.0 mg/cm2
  • Compaction density: 3.0 g/cm3
  • Active Material Proportion in Powder:95.5% (PVDF and Super P is 2% and 2.5%, respectively) 
Specific Capacity

 

 155 mAh/g (0.2C, 4.2-2.7 V vs Li/Li+, Half Cell)

500 Cycles @ 0.2C Charging/Discharging Rate [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]


Description

The NCM523-coated aluminum foil in a roll can be used as cathode for pouch cell testing. 

SPECIFICATIONS

NCM523 coating
  • Coating Thickness: ~88 um (double side coated) 
  • Total Thickness: ~103 um
    Foil Thickness: ~15-16 um
  • Width: 200mm (coating width of 175 mm, left and right-hand side is 12.5 mm without coating), Length: 20 m/roll
  • Double sides material density: 23.0 mg/cm2
  • Compaction density: 3.0 g/cm3
  • Active Material Proportion in Powder:95.5% (PVDF and Super P is 2% and 2.5%, respectively) 
Specific Capacity

 

 155 mAh/g (0.2C, 4.2-2.7 V vs Li/Li+, Half Cell)

500 Cycles @ 0.2C Charging/Discharging Rate [Electrolyte:1.0M LiPF6 in EC:DMC:EMC=1:1:1 Vol% with 1.0%VC]