$248.00
Li-Ion Battery Cathode - Aluminum Foil Single Side Coated by LiMn0.6Fe0.4PO4 (LMFP, 241mm L x 180mm W), 5 sheets/bag - bcaf-lmfpss—
$248.00
The Story
This electrode sheet is based on Aluminum foil coated by LiMn0.6Fe0.4PO4 (LMFP) in single side and is used as the cathode of Li-Ion battery - 5 sheets /bag
SPECIFICATIONS
-
Current collector (substrate): Aluminum foil (16 microns)
-
Cathode material: LiMn0.6Fe0.4PO4 (LMFP)
- Electrode Dimension: 241mm L x 180mm W
- Coated Area: 241mm L x 150mm W ( The edge width of blank area is 15 mm on both sides)
- Single Side Coating Area Density: 14.0±0.2 mg/cm2
- Compaction Density of Coating: 1.9 ±0.1g/cm3
- Current Collector Area Density: 4.05 mg/cm2
- Coating thickness: ~1 um
- Substrate thickness: 15 um
- Active Material Ratio in powder:94.9%
- Specific Capacity: 150 mAh/g at 0.1C
- Charging and Discharging Curve for the First Cycle
- Note: Please vacuum heated dry (80-100oC) before assembling the battery
for aluminum
for LiFePO4
Description
This electrode sheet is based on Aluminum foil coated by LiMn0.6Fe0.4PO4 (LMFP) in single side and is used as the cathode of Li-Ion battery - 5 sheets /bag
SPECIFICATIONS
-
Current collector (substrate): Aluminum foil (16 microns)
-
Cathode material: LiMn0.6Fe0.4PO4 (LMFP)
- Electrode Dimension: 241mm L x 180mm W
- Coated Area: 241mm L x 150mm W ( The edge width of blank area is 15 mm on both sides)
- Single Side Coating Area Density: 14.0±0.2 mg/cm2
- Compaction Density of Coating: 1.9 ±0.1g/cm3
- Current Collector Area Density: 4.05 mg/cm2
- Coating thickness: ~1 um
- Substrate thickness: 15 um
- Active Material Ratio in powder:94.9%
- Specific Capacity: 150 mAh/g at 0.1C
- Charging and Discharging Curve for the First Cycle
- Note: Please vacuum heated dry (80-100oC) before assembling the battery