Nickel Foam (300mm length x 80 mm width x 0.3 mm thickness) - EQ-bcnf-03—
$50.00
The Story
Specifications
-
Material: Nickel Foam, Purity> 99.99% (excellent anti-corrosive)
-
Sold in roll onlySurface Density: 346g/m^2
-
Length: 300 mm
-
Width: 80mm
-
Thickness: 0.3 mm
-
Net weight: 21g
-
- Porosity: ≥95% (80-110 Pores per Inch. average hole diameters about 0.25mm)
- Extensibility: Lengthwise≥5%; Widthwise≥12%
- Tensile StrengthLengthwise≥1.25N/mm^2; Widthwise≥1.00N/mm^2
- Notice: Please notice that it is normal to observe NiO peaks in the nickel foam in XRD data. It is really difficult to avoid the oxidation of the nickel.
- How to clean the Nickel Foam for Battery Cathode Substrate.
- It can be removed from the NiO by annealing in the hydrogen furnace.
-
Nickel foam (about 3.3 cm x 1 cm) was carefully cleaned with the concentrated HCl solution (37 wt.%) in an ultrasound bath for 5 min in order to remove the surface oxide layer. And then deionized water and absolute ethanol were used for 5 min each to ensure the surface of the Ni foam was well cleaned.
  Porosity: ≥95% (80-110 Pores per Inch, average hole diameter is about 0.25mm |
 Click the video above to see the battery cathode coated by MTI's Film coater MSK-AFA-II-VC |
 Other Metallic Foams |
Description
Specifications
-
Material: Nickel Foam, Purity> 99.99% (excellent anti-corrosive)
-
Sold in roll onlySurface Density: 346g/m^2
-
Length: 300 mm
-
Width: 80mm
-
Thickness: 0.3 mm
-
Net weight: 21g
-
- Porosity: ≥95% (80-110 Pores per Inch. average hole diameters about 0.25mm)
- Extensibility: Lengthwise≥5%; Widthwise≥12%
- Tensile StrengthLengthwise≥1.25N/mm^2; Widthwise≥1.00N/mm^2
- Notice: Please notice that it is normal to observe NiO peaks in the nickel foam in XRD data. It is really difficult to avoid the oxidation of the nickel.
- How to clean the Nickel Foam for Battery Cathode Substrate.
- It can be removed from the NiO by annealing in the hydrogen furnace.
-
Nickel foam (about 3.3 cm x 1 cm) was carefully cleaned with the concentrated HCl solution (37 wt.%) in an ultrasound bath for 5 min in order to remove the surface oxide layer. And then deionized water and absolute ethanol were used for 5 min each to ensure the surface of the Ni foam was well cleaned.
|
Porosity: ≥95% (80-110 Pores per Inch, average hole diameter is about 0.25mm |
Click the video above to see the battery cathode coated by MTI's Film coater MSK-AFA-II-VC |
Other Metallic Foams |